Structures by: Hewat E. A.
Total: 10
Ba2 Y Cu3 O6.23
Ba2Cu3O6.23Y
Solid State Communications (1987) 64, 301-307
a=3.8818Å b=3.8972Å c=11.8942Å
α=90° β=90° γ=90°
Ba2 Y Cu3 O6
Ba2Cu3O6Y
Solid State Communications (1987) 64, 301-307
a=3.8908Å b=3.8908Å c=11.9735Å
α=90° β=90° γ=90°
Ba2 Y Cu3 O5.72
Ba2Cu3O5.72Y
Solid State Communications (1987) 64, 301-307
a=3.8728Å b=3.8728Å c=11.9105Å
α=90° β=90° γ=90°
Tl2 Ca0.93 Ba1.96 Cu1.96 O8.17
Ba1.96Ca0.93Cu1.96O8.17Tl2
Physica C (Amsterdam) (1988) 152, 438-444
a=3.8558Å b=3.8558Å c=29.2596Å
α=90° β=90° γ=90°
Y Ba2 Cu3 O6.73
Ba2Cu3O6.73Y
Physica C (Amsterdam) (1990) 165, 419-433
a=3.8193Å b=3.8835Å c=11.6832Å
α=90° β=90° γ=90°
Y Ba2 Cu3 O6.58
Ba2Cu3O6.58Y
Physica C (Amsterdam) (1990) 165, 419-433
a=3.8252Å b=3.8786Å c=11.6987Å
α=90° β=90° γ=90°
Y Ba2 Cu3 O6.35
Ba2Cu3O6.35Y
Physica C (Amsterdam) (1990) 165, 419-433
a=3.858Å b=3.858Å c=11.7913Å
α=90° β=90° γ=90°
Y Ba2 Cu3 O6.45
Ba2Cu3O6.45Y
Physica C (Amsterdam) (1990) 165, 419-433
a=3.8293Å b=3.875Å c=11.7101Å
α=90° β=90° γ=90°
Trilead tristrontium copper(I) dicopper octaoxide chloride
ClCu3O8Pb3Sr3
Physica C: Superconductivity and Its Applications (Amsterdam, Netherlands) (1990) 167, 1-2 67-74
a=5.444(10)Å b=5.495(10)Å c=19.49(3)Å
α=90° β=90° γ=90°
Ba2 Y Cu3 O5.8
Ba2Cu3O5.8Y
Solid State Communications (1987) 64, 301-307
a=3.8801Å b=3.8801Å c=11.9391Å
α=90° β=90° γ=90°